| タイトル: | Fabrication of TiAl3 coating on TiAl-based alloy by Al electrodeposition from dimethylsulfone bath and subsequent annealing |
| 著者: | Miyake, Masao    https://orcid.org/0000-0001-8208-4030 (unconfirmed)Tajikara, Seiya Hirato, Tetsuji https://orcid.org/0000-0003-3030-1632 (unconfirmed) |
| 著者名の別形: | 平藤, 哲司 |
| キーワード: | Electroplating Organic solvent Aluminide Intermetallics Diffusion |
| 発行日: | Aug-2011 |
| 出版者: | Elsevier B.V. |
| 誌名: | Surface and Coatings Technology |
| 巻: | 205 |
| 号: | 21-22 |
| 開始ページ: | 5141 |
| 終了ページ: | 5146 |
| 抄録: | TiAl3 coating was formed on TiAl alloy by Al electrodeposition from a dimethylsulfone (DMSO2) bath and subsequent annealing. Before the Al electrodeposition, anodic dissolution of TiAl substrate in the DMSO2 bath was conducted to remove the surface oxide layer of the TiAl substrate. By performing the Al electrodeposition immediately after the anodic dissolution, uniform Al films adherent to the TiAl substrate could be obtained. Annealing at 650–1000 °C yielded a single TiAl3 layer or two layers of TiAl3 and TiAl2 on the TiAl substrate. The resulted TiAl3 layer was confirmed to show oxidation-resistance at high temperatures. |
| 著作権等: | © 2011 Elsevier B.V. This is not the published version. Please cite only the published version. この論文は出版社版でありません。引用の際には出版社版をご確認ご利用ください。 |
| URI: | http://hdl.handle.net/2433/143597 |
| DOI(出版社版): | 10.1016/j.surfcoat.2011.05.019 |
| 出現コレクション: | 学術雑誌掲載論文等 |
このリポジトリに保管されているアイテムはすべて著作権により保護されています。