High-density excitation effect on photoluminescence in ZnO nanoparticles

Abstract

In this study, photoluminescence PL under high excitation intensity as a function of crystalline size was systematically investigated through ZnO nanocrystalline films prepared by spin-coating a colloidal solution of ZnO nanoparticles obtained using the microemulsion method. Annealing of the films at 723, 633, and 593 K allowed us to tune the crystalline radius R. PL studies distinguished different regimes of crystalline size according to the ratio of R to the effective Bohr radius aB R/aB. For the sample annealed at 723 K R/aB=7.2 , the peak of stimulated emission due to the exciton-exciton collisions appeared on the low-energy side of the exciton emission with an increase in excitation intensity. A further increase in excitation intensity eventually resulted in the occurrence of an electron-hole plasma EHP accompanied by consequent band gap renormalization, which indicates that high excitation intensity provokes the dissociation of excitons. For the sample annealed at 633 K R/aB=4.7 , the stimulated emission was observed while the transition to EHP was obscure. For the sample annealed at 593 K R/aB=2.1 , only emissions due to the recombination of the electron-hole pair were observed, and stimulated emission did not appear even when the excitation intensity was increased. The transition from free-exciton emission to donor-bound exciton emission was observed in temperature dependence of PL only for the sample with R/aB=7.2. The origin of annihilation of the stimulated emission with a size reduction is discussed based on nonradiative Auger recombination.