タイトル: | Visible to near infrared conversion in Ce3+-Yb3+ Co-doped YAG ceramics |
著者: | Ueda, Jumpei https://orcid.org/0000-0002-7013-9708 (unconfirmed) Tanabe, Setsuhisa https://orcid.org/0000-0002-7620-0119 (unconfirmed) |
著者名の別形: | 上田, 純平 |
発行日: | 17-Aug-2009 |
出版者: | American Institute of Physics |
誌名: | Journal of Applied Physics |
巻: | 106 |
号: | 4 |
開始ページ: | 043101 |
抄録: | In Ce3+–Yb3+ co-doped Y3Al5O12 (YAG) ceramics, possibility of quantum cutting mechanism converting one visible photon into two NIR photons with optimum quantum efficiency approaching 200% have been investigated. In this material, Yb3+ emissions due to the 2F5/2-2F7/2 in the range of 1 μm were observed upon the excitation of 5d level of Ce3+. In addition, excitation spectra of Yb3+ emission corresponded to that of Ce3+ emission completely. Lifetime of the 5d level of Ce3+ decreased with increasing Yb3+ content. These results indicate the energy transfer (ET) from the 5d levels of Ce3+ to the 5F5/2 level of Yb3+. In (Y0.945Ce0.005Yb0.05) 3Al5O12 sample, the directly measured quantum yield (QY) of Yb3+ emission upon the excitation of 5d level of Ce3+ was about 12% and lower than QY (96%) that estimated from the ET efficiency which was calculated with the measured lifetime of Ce3+. |
著作権等: | Copyright c 2009, American Institute of Physics |
URI: | http://hdl.handle.net/2433/150457 |
DOI(出版社版): | 10.1063/1.3194310 |
関連リンク: | http://jap.aip.org/resource/1/japiau/v106/i4/p043101_s1 |
出現コレクション: | 学術雑誌掲載論文等 |
このリポジトリに保管されているアイテムはすべて著作権により保護されています。