| タイトル: | Iron Aluminide Coatings by Electrodeposition of Aluminum from an Organic Bath and Subsequent Annealing |
| 著者: | Miyake, Masao    https://orcid.org/0000-0001-8208-4030 (unconfirmed)Motonami, Hiroshi Hirato, Ttetsuji |
| 著者名の別形: | 三宅, 正男 元波, 洸 平藤, 哲司 |
| キーワード: | electroplating organic solvent aluminizing heat treatment intermetallics |
| 発行日: | 2012 |
| 出版者: | Iron and Steel Institute of Japan |
| 誌名: | ISIJ International |
| 巻: | 52 |
| 号: | 12 |
| 開始ページ: | 2273 |
| 終了ページ: | 2277 |
| 抄録: | Oxidation-resistant Fe–Al alloy coatings were formed on Fe substrate by a process using electrodeposition of Al and annealing. Electrodeposition in a dimethylsulfone-aluminum chloride bath containing an additive at 110°C yielded a dense Al layer adherent to the Fe substrate. Annealing of the Fe substrate with the electrodeposited Al layer generated an Fe2Al5 layer on the surface at 700°C and 800°C, and an FeAl layer at 900°C through interdiffusion. Oxidation tests at 600°C and 800°C confirmed that the FeAl layer formed through the process could act as an oxidation-resistant coating. |
| 著作権等: | © 2012 by The Iron and Steel Institute of Japan Publisher permitted to deposit this paper on this repository. 発行元の許可を得て登録しています |
| URI: | http://hdl.handle.net/2433/237638 |
| DOI(出版社版): | 10.2355/isijinternational.52.2273 |
| 出現コレクション: | 学術雑誌掲載論文等 |
このリポジトリに保管されているアイテムはすべて著作権により保護されています。