Title: Evaluation of magnetic properties in ferromagnetic martensite particle using type 304 stainless steel wire
Authors: Kinoshita, K.
Author's alias: 木下, 勝之
Issue Date: 1-Jan-2020
Publisher: American Institute of Physics Inc.
Journal title: AIP Advances
Volume: 10
Thesis number: 015313
Abstract: In this study, the magnetic properties of a single martensite particle were investigated using type 304 stainless wire, which can reduce the number of crystal grains per unit area. First, the magnetization curve of wire specimens with different martensite fractions was measured by a SQUID magnetic flux meter. Then, the coercivity and susceptibility parameters were evaluated from the magnetization curve and factors contributing to these parameters were discussed. It was found that the coercivity values along the long and short axes of wire specimens with a diameter of 0.4 mm increased and subsequently decreased with an increase in the martensite fraction. Further, the susceptibility values of the same specimen along the long axis increased and along the short axis decreased with increasing martensite fractions. The results indicate that the coercivity and susceptibility of a martensite particle are affected by the size of variant clusters and the shape anisotropy of the martensite particle.
Description: This paper was presented at the 64th Annual Conference on Magnetism and Magnetic Materials.
Rights: All article content, except where otherwise noted, is licensed under a Creative Commons Attribution (CC BY) license (
DOI(Published Version): 10.1063/1.5131048
Appears in Collections:Journal Articles

Show full item record

Export to RefWorks

Export Format: 

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.