Evaluation of termite resistance of medium density fiberboard (MDF) manufacture from agricultural fiber bonded with citric acid

Abstract

Nowadays, the use of agricultural fibers for panel composite materials attracts great intention. Further, it is desirable to develop of natural adhesive derived from non fossil resources to be safe adhesive without using harmful chemical substances. In this study, citric acid application as natural adhesive was investigated for medium density fiberboard (MDF) manufacture from pineapple leaf fiber. The ratio of citric acid and sucrose and adhesive content was 25–75 and 20 wt%, respectively. Two different types of board consisting of three layers with target density of 0.8 gr/cm³ were prepared. The board was hot pressed at 200 °C and 4.5 MPa for 10 min.Additionalboards with same structure were prepared using citric acid only. The biological properties of the boards such as their resistance against subterranean termite attack have been examined. The results indicate that generally, there was a significant effect of impregnation with mixture of citric acid and sucrose and citric acid only on the susceptibility of the MDF board specimens. With regards to the percentage of specimen mass losses, fiber orientation had no significant effect on the termite resistance against Coptotermes formosanus Shiraki. Utilization of natural adhesive, citric acid was promising to be used for MDF manufacturing. Our findings show that the total adhesive content of 20% of the type a board could be used for agricultural fiber product applications to protect structures from degradation by termites.