タイトル: | On the Age-hardening of Aluminium-rich Al-Zn alloys |
著者: | Nishimura, Hideo |
発行日: | 1-Jul-1924 |
出版者: | College of Engineering, Kyoto Imperial University |
誌名: | Memoirs of the College of Engineering, Kyoto Imperial University |
巻: | 3 |
号: | 6 |
開始ページ: | 133 |
終了ページ: | 163 |
抄録: | (1) The phenomena of age-hardening were observed on the Al-rich Al-Zn alloys, when the zinc content exceeded 5%, and these alloys were divided into 2 kinds at 26% zinc, according to their properties. (2) Al-Zn series showed an eutectoid transformation at 256°C, and this transformation was observed on the alloys containing more than 20% zinc. The solubility of zinc in aluminium was found to be less than 5% at 110°C. Owing to these facts, the equilibrium diagram on the aluminium side was obtained. (3) It was found that age-hardening did not always concern a compound. The question is the solubility of a solid solution. (4) Age-hardening was considered to be due to the spontaneous crystallisation of a super-cooled solid solution. With this conception, the phenomena of hardening were explained. (5) As the mechanism of hardening it was found that the separaticn of a second phase in finely divided perticles gave rise to hardening on the one side, and on the other the disintegration of the grains. |
URI: | http://hdl.handle.net/2433/280058 |
出現コレクション: | Vol.3 No.6 |
このリポジトリに保管されているアイテムはすべて著作権により保護されています。