Title: Structural relaxation of Lix(Ni₀.₈₇₄Co₀.₀₉₀Al₀.₀₃₆)O₂ after Lithium Extraction down to x = 0.12
Authors: Kang, Jian
Takai, Shigeomi
Yabutsuka, Takeshi
Yao, Takeshi
Author's alias: 高井, 茂臣
薮塚, 武史
八尾, 健
Keywords: lithium ion battery
NCA
relaxation analysis
Issue Date: Aug-2018
Publisher: MDPI AG
Journal title: Materials
Volume: 11
Issue: 8
Thesis number: 1299
Abstract: A structural relaxation study has been carried out on Lix(Ni₀.₈₇₄Co₀.₀₉₀Al₀.₀₃₆)O₂ after the electrochemical lithium was extraction down to x = 0.12. These relaxation analyses have been carried out using X-ray diffraction coupled with the Rietveld analysis, assuming two phases (H2 and H3) and co-existence with R3̅m symmetry. The mole fraction of the H3 phase seemed not to vary largely during the relaxation time. As for the lattice constants, both H2 and H3 phases gradually increased the a-axis with the relaxation time. On the other hand, H2 and H3 phases increased and decreased the c-axis, respectively. The results are compared with that of previously reported Ni-rich NCA.
Rights: © 2018 by the authors. Licensee MDPI, Basel, Switzerland. This article is an open access article distributed under the terms and conditions of the Creative Commons Attribution (CC BY) license (http://creativecommons.org/licenses/by/4.0/).
URI: http://hdl.handle.net/2433/235485
DOI(Published Version): 10.3390/ma11081299
PubMed ID: 30060491
Appears in Collections:Journal Articles

Show full item record

Export to RefWorks


Export Format: 


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.